Shades: A1 / A2 / A3 / A4 / B1 and semi-transparent
Packaging size: 8g double cartridge
Accessories: Mixing tips
Storage: 3-9°C (Keep refrigerated)
Technical Data
| Vickers hardness | >549 MPa |
| Compressive strength | >290 MPa |
| Flexural strength | >118 MPa |
| E-Module | >12039 MPa |
| Tensile strength | 45 MPa |
| Radiopacity | 210% |
| Polymerisation | 7-9 Minutes |
Dual Cure Universal Resin Cement - HEYTEC CemX
HEYTEC CemX is a dual-cure, highly radio-opaque, fluorescent and highly abrasion-resistant flowable self-adhesive resin cement for various types of indications such as all-ceramic, composite or metal inlays, onlays, crowns and bridges, posts, 3-unit inlay/onlay bridges, all-ceramic, 2 -or 3-unit maryland bridges and veneers plus HEYTEC CemX can also used for core build up.
HEYTEC CemX is the latest generation of self-adhesive resin cements.
Comfortable and easy delivery in automix syringe.
- Compares to: RelyX Ultimate (3M)
Features
| Features | Benefits |
|---|---|
| One material for three indications | Optimal "interface" between pin-cement-dentin-crown |
| High viscosity | Very comfortable handling |
| Automix cartridge | Direct and ergonomic application/no mixing necessary |
| Highly radiopaque | X-ray check possible |
| High filler content | Highly abrasion resistant |
| Excellent physical data | Long-lasting restorations and extremely low shrinkage |
| Dual-cure | Curing can be accelerated with a polymerisation light |
| Does not contain Bis-GMA | Optimised biocompatability |
Shades: Bleach X /A1 / A2 / A3 / transparent
Packaging size: 2g syringe
Accessories: tips
Storage: room temperature
Light Cure Veneer Cement - HeyTEC Cem Veneer
HeyTEC Cem Veneer is a light-cure, single component, highly radiopaque luting material for cementing porcelain, composite and ceramic veneers and for cavity lining. HeyTEC Cem Veneer is BisGMA, Bis EMA and TEGDMA free and highly viscous.
HeyTEC Cem Veneer offers easy handling and excelent color stability for highly esthetic veneer cases.
- Compares to: RelyX Veneer (3M)
Technical Data
| Filler Content | 80% |
| Compressive strength | >362 MPa |
| Flexural strength | >140 MPa |
| E-Module | >14900 MPa |
| Film thickness | 28 µm |
| Radiopacity | 210% |
| Viscosity | 590 Pas |
| BisGMA | no |
| BisEMA | no |
| TEGDMA | no |
Features
| Features | Benefits |
|---|---|
| High viscosity | Very comfortable handling |
| Light cure only | excellent color stability |
| Highly radiopaque | X-ray check possible |
| High filler content | Highly resistant |
| Excellent physical data | Long-lasting restorations and extremely low shrinkage |
| Does not contain Bis-GMA | Optimised biocompatability |
- Package includes: 1 x 5ml HeyTec Cem SE Minimix, 5 x mixing tips
Selfetching Cement - HeyTec Cem SE
HeyTec Cem SE is a self-adhesive dual-cure luting cement for permanent cementations. When HeyTec Cem SE is used, conditioning and bonding of the tooth structure are not necessary.
ETCHING, PRIMING, BONDING, DESENSITISING AND CEMENTATION IN JUST A SINGLE WORKING STEP
...the latest cement generation!
- Compare to: SpeedCEM (Ivoclar Vivadent), MaxCem Elite (Kerr), G-Cem (GC)
High adhesion strength without etching, conditioning or bonding
The entire procedure of cementation requires just a few steps, with no risk, dentin overetching or or sensitivity. The product is self neutralizing - with an initial low pH that increases after the application to 5.5 pH in a few hours. This rise in pH prevents post cementation sensitivity.
Perfect fit reconstruction and predictable work
Thin film - 12um - provides precise cementation while delicate expansion of cement eliminates its shrinkage from the margins. This ensures excellent marginal integrity. The dual cure system allows pre-curing of the positioned restoration, as well as easy removal of excess in its initial flexible phase.
Excellent color stability and natural fluorescence
Proven color stability is satisfying even for transparent ceramics, this guarantees a long-lasting aesthetic effect. An additional advantage is the significant release of fluoride, which results in strengthening the surrounding tissues.
- Package includes: 1 x 5ml HeyTec SEMI MINIMIX, 5 x mixing tips
- Compare to: Systemp.link (Ivoclar Vivadent), Premier Implant (Premier), Implantlink Semi (Detax)
Semi permanent cement - HeyTec Semi
HeyTec SEMI is a dual-curing, semi-permanent cement for the cementation of crowns and bridges on implants and natural teeth. No chemical adhesion [0 MPa] is compensated by controlled expansion of the cement. This ensures optimal fastening, and removal of the restoration without any damage.
Technical specifications
Compressive strength - 40 MPa
Film thickness - 20 um
Processing time (23 ° C / 73 ° F) - 2:00 min.
Setting time (self-curing) - approx. 4:00 min.
Light curing - 40 sec per area
Thin layer and controlled expansion
precise fit is guaranteed by a thin layer of HeyTec SEMI (<20?). Controlled volume expansion of the cement (eliminates the shrinkage). All this gives an ideal marginal sealing.
The flexible structure for the bone and implant protection
Stress-absorbing properties are much higher due to the retained flexibility of HeyTec SEMI (40MPa). This creates a much better environment for tissue regeneration.
Excellent "snap-off" for revisions
Revision or prosthetic reconstruction removal is safe and easy. HeyTec SEMI application does not require etching, conditioning or bonding, which eliminates the chemical connection between the abutment and crown. Cement residue can be easily removed and the construction recemented if necessary.
Biocompatible and antibacterial
HeyTec SEMI is eugenol free, has a neutral taste and smell for patient comfort and added zinc oxide causes an antibacterial effect.